Effect of surfactant concentration and solvent used for washing in the preparation of Yb:Y2O3 transparent ceramics Текст научной статьи по специальности «Химические науки»

CC BY
172
35
i Надоели баннеры? Вы всегда можете отключить рекламу.
Ключевые слова
TRANSPARENT CERAMICS / YB:Y2O3 / SURFACTANT

Аннотация научной статьи по химическим наукам, автор научной работы — Deshmukh Pratik, Satapathy S., Singh M.K., Gupta P.K.

Nanoparticles of Yb:Y2O3 have been synthesized by coprecipitation synthesis routes. The (NH4)2SO4 surfactant was added to Y(OH)3 precipitate during synthesis to control the size, morphology, agglomeration and phase of nanoparticles. The dried precipitates were calcined at 900 ° C to obtain the desired cubic phase Yb:Y2O3 nano particles. In the present study we reported the effects of surfactant concentration on size, morphology, agglomeration and phase of Yb:Y2O3 nanoparticles. However the addition of surfactant is not enough to get non-agglomerated nanoparticles. The extracted precipitate should be washed in proper solvent to avoid formation of hard agglomerate during drying. Hence the effects of washing solvent (i.e. water and methanol) on agglomeration and transparency were also reported. The transparency of the sintered pellets, prepared by varying the surfactant concentration and washing solvent, was evaluated. A transparency of 80 % at 1500 nm was achieved in 1 mm thick Yb:Y2O3 ceramic pellet by optimization of the surfactant and washing solvent.

i Надоели баннеры? Вы всегда можете отключить рекламу.
iНе можете найти то, что вам нужно? Попробуйте сервис подбора литературы.
i Надоели баннеры? Вы всегда можете отключить рекламу.

Текст научной работы на тему «Effect of surfactant concentration and solvent used for washing in the preparation of Yb:Y2O3 transparent ceramics»

NANOSYSTEMS: PHYSICS, CHEMISTRY, MATHEMATICS, 2016, 7 (3), P. 534-537

Effect of surfactant concentration and solvent used for washing in the preparation of Yb:Y2O3 transparent ceramics

Pratik Deshmukh*, S. Satapathy**, M.K. Singh, P.K. Gupta

Nano Functional Materials Laboratory, Laser Materials Development & Devices Division, Raja Ramanna Centre for Advanced Technology, Indore 452013, India * [email protected], ** [email protected]

PACS 81.20.Ev; 78.67.Bf; 42.70.Hj DOI 10.17586/2220-8054-2016-7-3-534-537

Nanoparticles of Yb:Y2O3 have been synthesized by co-precipitation synthesis routes. The (NH4)2SO4 surfactant was added to Y(OH)3 precipitate during synthesis to control the size, morphology, agglomeration and phase of nanoparticles. The dried precipitates were calcined at 900 °C to obtain the desired cubic phase Yb:Y2O3 nano particles. In the present study we reported the effects of surfactant concentration on size, morphology, agglomeration and phase of Yb:Y2 O3 nanoparticles. However the addition of surfactant is not enough to get non-agglomerated nanoparticles. The extracted precipitate should be washed in proper solvent to avoid formation of hard agglomerate during drying. Hence the effects of washing solvent (i.e. water and methanol) on agglomeration and transparency were also reported. The transparency of the sintered pellets, prepared by varying the surfactant concentration and washing solvent, was evaluated. A transparency of ~ 80 % at 1500 nm was achieved in 1 mm thick Yb:Y2O3 ceramic pellet by optimization of the surfactant and washing solvent.

Keywords: transparent ceramics, Yb:Y2O3, surfactant.

Received: 4 February 2016

1. Introduction

Nanotechnology and sintering techniques can be utilized in combination for the fabrication of rare earth-doped yttria transparent ceramics because the high surface area of the nanoparticles facilitates sintering, permitting one to reach full density more rapidly at temperatures far below the melting point of the material [1,2]. The fabrication of Yb doped Y2O3 transparent ceramic involves the synthesis of non-agglomerated nanoparticles of Yb doped Y2O3 and sintering of pressed pellets (prepared using a nanopowder) at high temperatures under low pressure [3]. Of the different methods adopted for the preparation of non-agglomerated nanoparticles, the co-precipitation method has been widely used for nanopowder synthesis because the particle size and morphology can be efficiently controlled [4].

However, in case for the synthesis of Yb:Y2O3 nanopowders using co-precipitation method, the Y(OH)3 precipitate underwent severe agglomeration during drying. This agglomeration led to poor sinterability for the Yb:Y2 O3 nanopowder obtained after calcination. Thus, special measures were adopted during precipitation, such as addition of surfactant to create non-agglomerated nanoparticles. It is reported that the surfactant (NH4)2SO4, which adsorbs on the surface of the Y(OH)3, hinders the bonding between particles [5,6]. It has also been shown that the morphology of precursors was affected by the [(NH4)2SO4]/[Nd:Y2O3] ratio (measured by weight) [7]. However, the effect of surfactant concentration on the crystallographic phase of the prepared nanopowder has not been investigated yet. Similarly, the solvent used to wash the precipitate plays a crucial role in the agglomeration of nanoparticles. Some solvents remove the surfactant from the particle surface and cause hard agglomeration during drying of precipitate [8]. The chemical nature of the washing solvent may be different for dissimilar oxide nano particles.

Thus, the aim of this work is to study the effect of surfactant concentration on the size, morphology, agglomeration and phase of Yb:Y2O3 nanoparticles obtained using the co-precipitation method as well as its influence on the transparency of sintered pellets incorporating these nanoparticles. The effect of the solvent used for washing the precipitate on the transparency of the pellet is also evaluated.

2. Experimental

A 0.2 M mother solution of Yb doped (1 mol%) Y2O3 (using Yb2O3 and Y2O3 powders of purity 99.99 %; make: Alfa Aesar) was prepared by dissolution with dilute nitric acid. The mother solution was titrated with 1 M aq. ammonia by normal striking. A white jelly like basic Yb:Y(OH)3 precipitate was formed during the titration which was controlled by measuring online pH. After aging, the hydroxide precipitate was divided into five equal parts. In order to investigate the effects of surfactant concentration on the transparency of sintered Yb:Y2O3 pellets, (NH4)2SO4 surfactant having 5, 10, 15, 20 and 30 wt% concentration was added to each part of the precipitate separately i.e. 5 wt% of (NH4)2SO4 solution were added into first part of hydroxide precipitate and so

on. Then, the samples were washed using methanol and dried in an oven. Calcination was performed at 900 °C for 4 h in air. Then, the calcined powders were pressed under a pressure of 150 MPa using a uniaxial press. To show only the effect of morphology and particle size distribution on pellet's transparency, a cold isostatic press (CIP) was not used for pellet pressing. The pellets were sintered at 1750 ° C for 5 h using a high temperature high vacuum furnace with a tungsten mesh heating element (Hind High Vacuum High Temperature Furnace, Hind High Vac. Co (P). Ltd., Bangalore). Finally, the pellets were polished using 300 nm alumina powders. Phase identifications of the Yb (1 mol%):Y2O3 nanopowders prepared using different surfactant concentrations were performed using X-ray diffractometry (XRD) (Cu-Ka, Rigaku) and morphology was observed by field emission scanning electron microscope (FESEM, Zeiss).

3. Results and discussion

X-ray diffraction (XRD) patterns of Yb(1 mol%):Y2O3 powders prepared using different surfactant concentrations are shown Fig. 1. The XRD patterns of these powders are in good agreement with that of Y2O3 (Standard JCPDS, Card no. 41-1105) crystal [9,10]. The results revealed that the precursor transformed to cubic phase of Y2O3 crystals after calcination at 900 °C for 5 wt% and 10 wt% of surfactant concentration but for 15 wt% and above surfactant concentrations, it transforms to a mixed phase i.e. combination of cubic and monoclinic phase Y2O3 crystal. The reflection from the monoclinic phase (space group C2/m) (Y2O3: PDF 44-0399) appeared in the diffraction patterns for 15, 20 and 30 wt% surfactant concentration as shown in Fig. 1 [10].

XRD Patterns Of Yb(1%):Y20.

m

—•—I—■—t—■—I—■—I—1—I—1—I—■—I • I—I—1—

20 25 30 35 40 45 50 55 60 55 TO

20 (degree)

Fig. 1. X-ray diffraction patterns of Yb (1 mol%):Y2O3 nanopowders prepared using different surfactant concentrations: (a) 5 wt%, (b) 10 wt%, (c) 15 wt%, (d) 20 wt % and (e) 30 wt%

Scanning electron micrographs of Yb (1 mol%):Y2O3 powder prepared using different surfactant concentrations are shown in Fig. 2. The morphologies of the Yb (1 mol%):Y2O3 nanoparticles are nearly spherical and are unchanged with variation in surfactant concentration. The existence of so2- on the surface of yttrium hydroxide precursors at comparatively high temperature inhibits volume diffusion and/or grain boundary diffusion, and then particle growth proceeds by surface diffusion or evaporation-condensation, which results in collapse of agglomerates into well-dispersed nanopowders [12].

Photographs of sintered pellets of Yb (1 mol%):Y2O3 prepared using different surfactant concentrations i.e. (a) 5 wt%, (b) 10 wt%, (c) 15 wt%, (d) 20 wt% and (e) 30 wt% are shown in Fig. 3. As is clearly visible, the transparency of the sample (a) and (b) is so good, as to allow the easy reading of the underlying print, however, the transparency does seem to be decreased at higher surfactant concentrations. This may be due the transformation of the phase from cubic to a mixed one (as evident from Fig. 1).

Figure 4 shows the photograph of sintered pellet of Yb (1 mol%):Y2O3 prepared by using 5 wt% concentration of surfactant and water as the washing solvent. The simple change in washing solvent from methanol to water during synthesis would appear to lead to a drastic decrease in the transparency of the sintered Yb (1 mol%):Y2O3 pellet. This is due to the formation of high strength agglomerates after washing with the liquid having higher surface tension like water (greater than methanol) [13].

Using the above experimental conditions, we have successfully fabricated highly transparent Yb (1 mol%): Y2O3 ceramics pellets (transparency ~ 80 % in visible-IR region without considering Fresnel's reflection).

536

Pratik Deshmukh, S. Satapathy, M. K. Singh, P. K. Gupta

4 j *4 * * * * %

loom (Mr ■ 10 W5 NW aflMtA.St: (Mall Fall 20K ffff I WO* ■Onim itafl*4&OOKX NIM 1*0 MRC«t m | lQOrm EHr.lOHkV agnalA.St:: (M»MF.bHit I WO-BJmm Mag- 40OOKX NFM Ut AftCAT )Hfl| |

M n 1 K. - - r $ t N V r «

TOinm EMT.IOOOkV t^MA-tHH DM* 11 Fab »IB ff1^ WO-BJirm Mag ■ 44MKX WM LAB HftCAT pHU "" EWT* (QMW !»•«■» [)«.,-..„:«,., MB .■JO ■ IiT„ Uaq-40.00KX HrH IM HRCAT |H||

v A* «i Jk * ■» A * V * ^

iMom EOT ■ ISOOkV S^nHA'SIS? M»l1FM20tb ffiflU I H WO«»2mm mB-40«KX NFM LAB BBCAT p|| |

Fig. 2. FESEM images of Yb (1 mol%):Y2O3 nano powders prepared using different surfactant concentrations: (a) 5 wt%, (b) 10 wt%, (c) 15 wt%, (d) 20 wt% and (e) 30 wt%

Fig. 3. Photograph of sintered pellets of Yb(1 mol%): Y2O3 prepared using different surfactant concentrations: (a) 5 wt%, (b) 10 wt%, (c) 15 wt%, (d) 20 wt% and (e) 30 wt%

Yb:/203

Fig. 4. Photograph of sintered pellet of Yb(1 mol%): Y2O3 prepared using 5 wt% of surfactant concentration and water as the washing solvent

Wavelength (nm)

Fig. 5. Optical transmittance spectrum of a sintered pellet of Yb (1 mol%): Y2O3 and inset shows the photograph of transparent ceramic

4. Conclusion

The use of surfactant (NH4)2SO4 during the synthesis of nanoparticles is helpful to control particle size and agglomeration. The excess concentration of it does not affect the particle morphology. Hence, the sinterability (which mainly depends on the size, agglomeration and morphology of the particles) of the all samples (prepared using different (NH4 )2SO4 concentrations) would remained same. Thus, the observed difference in transparency of Yb (1 mol%):Y2O3 sintered pellets is due to transformation of the phase from cubic to mixed (i.e. combination of cubic and monoclinic phase). Additionally, the surface tension of washing solvent affects the agglomeration during drying of the precipitate. The optimized synthesis parameters for Yb:Y2O3 nanoparticles i.e. 5 wt% surfactant concentration and methanol as washing solvent have been used to successfully fabricate highly transparent Yb (1 mol%):Y2O3 ceramics pellets.

References

[1] Lu J., Lu J., et al. Nd3+:Y2O3 ceramic laser. Japanese Journal of Applied Physics, 40(2001), P. L1277-L1279.

[2] Shirakawa A., AkaichiK., et al. First mode-locked ceramic laser: femtosecond Yb3+: Y2O3 ceramic laser. Laser Physics, 2004, 14(11), P. 1375-1381.

[3] Ikegami T., Mori T., et al. Fabrication of Transparent Yttria Ceramics through the Synthesis of Yttrium Hydroxide at Low Temperature and Doping by Sulfate Ions. J. Ceram. Soc. Jpn., Int. Ed., 1999, 107(3), P. 297.

[4] Ji-Guang Li, Takayasu Ikegami, et al. Co-precipitation synthesis and sintering of yttrium aluminum garnet (YAG) powders: the effect of precipitant. Journal of the European Ceramic Society, 2000, 20, P. 2395-2405.

[5] Saito N., Matsuda S-I., Ikegami T. Fabrication of transparent yttria ceramics at low temperature using carbonate-derived powder. J. Am. Ceram. Soc., 1998, 81(8), P. 2023-2028.

[6] Lu J., Ueda K.I.,et al. Neodymium doped yttrium aluminum garnet (Y3Al5Oi2) nanocrystalline ceramics-a new generation of solid state laser and optical materials J. Alloys Comp, 2002, 341, P. 220-225.

[7] Wang H.Z., Gao L., Niihara K. Synthesis of nanoscaled yttrium aluminum garnet powder by the co-precipitation method. Mater Sci. Eng., 2000, A288, P. 1.

[8] Gao L., Qiao H.C., Qiu H.B., Yan D.S. Preparation of Ultrafine Zirconia Powder by Emulsion Method. J. Eur. Ceram. Soc., 1996, 16, P. 437.

[9] Wen L., Sun X., et al. Synthesis of yttria nanopowders for transparent yttria ceramics. Opt. Mater., 2006, 29, P. 239.

[10] Gajovic A., Tomasic N., et al. Influence of mechanochemical processing to luminescence properties in Y2O3 powder. J. Alloys and Compd, 2008, 456, P. 313-319.

[11] JCPDS International Centre for Diffraction DATA, Swarthmore, PA, 1996.

[12] Takayasu I., Li J.G., Sakaguchi I., Hirota K. Morphology change of undoped and sulfate-ion-doped yttria powders during firing. J. Am. Ceram. Soc., 2004, 87(3), P. 517-519.

[13] Mouzon J., Oden M., Tillement O., Jorand Y. Effect of drying and dewatering on yttria precursors with transient morphology. J. Am. Ceram. Soc., 2006, 89(10), P. 3094-3100.