Optical Analysis of Ag-NPs Containing Methyl Ammonium Lead Tri-Iodide Thin Films
Cliff Orori Mosiori Walter Kamande Njoroge 2, Lawrence Otieno Ochoo 2
1 Technical University of Mombasa
P. O. Box 90420-80100, Mombasa, Kenya
2 Kenyatta University
P. O. Box 43844-00100, Nairobi, Kenya
DOI: 10.22178/pos.26-10
LCC Subject Category:
TP155-156, QC450-467, QD450-801
Received 12.07.2017 Accepted 12.09.2017 Published online 30.09.2017
Corresponding Author: [email protected]
© 2017 The Authors. This article is licensed under a Creative Commons Attribution 4.0 License
Abstract. Methyl ammonium lead tri-iodide hybrid thin films were grown using solution technique. They were doped with silver nano-particles at different concentrations at concentrations of 0.05, 0.06, 0.07, 0.08, and 0.09 mM. Their reflectance and transmittance were recorded in the wavelength range 300-900 using UV-Vis double - beam spectrophotometer. Using these measurements, other optical parameters were simulated using scout software. The effect of silver nanoparticles was investigated. Results revealed that the thin films had highest transmittance of about 79 % as their band gap varied from 1.921-1.832 eV. Electrical conductivity varied from 1.4-1.6x105 S cm-1 while optical conductivity varied in the range of 0.3-0.6x1010 sec-1. They had a significantly low refractive index, suitable for optical applications within the range of 1.6-1.8. The extinction coefficient varied in the range as 1.0-1.7*10-5 while the absorption coefficient varied varies in the range of 2.1-4.2 cm- 1. It was concluded that the thin films were suitable for photonic device applications.
Keywords: optical parameters; silver nano-particles; methyl ammonium lead tri-iodide; CH3NH3PbI3; energy band gap.
INTRODUCTION
Hybrid nonlinear optical materials have received much interest because of their potential applications in optical devices such as optical signal processing, optical switching and optical power limiting [1, 4, 21]. Hybrid materials are currently attracting considerable attention and they are emerging as a new front runner promising materials for optical devices applications owing to their high nonlinearity and ultra-fast responses. These are qualities required in many scientific and material technology device applications [8, 22]. Hybrid materials can be modified when they are doped using suitable metal nanoparticles to display unique optical nonlinearities. In this study, silver nanoparticles were chosen because have excellent unique nonlinear optical properties. Silver as a dopant in methyl ammonium lead tri-iodide, it may contribute to its nonlinear to offer several characteristics advantages like flexibility, ease of fabrication, good transparency or non linear reflectivity, photo and thermal sta-
bility [3, 19, 24]. Low fabrication cost may be an added advantage. Scientific developments have developed various techniques to prepare the hybrid films [10, 28, 29]. Among them is solution technique which is a very good, simple, and easy to prepare the hybrid films. It is a technique that was employed to grow silver containing methyl ammonium lead tri-iodide hybrid films at different concentrations. This work reports on the optical properties of CHsNHsPbh, as modified by silver nanoparticles as simulated using the scout software.
THEORETICAL FRAMEWORK
It's generally accepted that in thin or thick films or wafers, linear absorption coefficient a of an optical medium is usually described by the Lem-bert-Beer law [7] as (1):
I = I e~aL. (1)
0 v J
This is acceptable that absorbance A can be defined as (2):
A = 10/1.
So that Equation (2) can be written as (3):
(2)
A = e
aL
(3)
From the Equation (3) absorption coefficient takes the form (4) :
a = 2.303 A, (4)
L
where I0 - is the incident light intensity;
A - is absorbance; I - is the transmitted light intensity; L - is the length of the absorbing medium.
The extinction coefficient k of the medium sample is directly proportional to the absorption coefficient a according to the following Equation (5):
k =
aX 4n '
(5)
where A - is the wavelength of incident light [15].
Based on this concept, the refractive index n is fundamental parameters as it relates the properties of material as [20]:
n =
1 + R ' 1 - R
+
4R
(1 - R)2
K
1/2
(6)
where the optical reflectance R of the material is given by the relation [15]:
R = [l - (TeeL )J
/2
(7)
Optical conductivity and refractive index of the material relates as [30]:
°opt =
anc 4n
(8)
where c - is the velocity of light, then electrical conductivity <Je[ect of the material is related to its optical conductivity <Jopt as [32]:
&opt =
2XG.
opt
a
(9)
Finally, the optical energy gap E between the
valence band VB and the conduction band CB of any material relates to the absorption coefficient a and the incident photon energy hv according to the following relation (10):
(ahv ) = C (hv - E Y
(10)
where h - is the Planck's constant;
v - is the frequency of incident photons;
C - is a constant, its value depends on the transition probability;
m - is an index, its value depends on the type of the electronic transition [12].
METHODOLOGY Material and Chemicals
Silver nitrate AgNO3, hydrazine hydrate, sodium citrate and sodium dodecyl sulphate, double-distilled de-ionized water, Potassium chloride KCl, zinc nitrate Zn(NO3)2.6H2O, copper sulfate CuSO4.5H2O, absolute ethyl alcohol CH3CH2OH, ethylene glycol Aft, sodium hydroxide NaOH, sodium borohydride NaBH4, ascorbic acid CôHsOô, trisodium citrate CeHsNa3O7.2H2O, ammonia NH3, poly vinyl alcohol PVA among others.
Preparation of silver nanoparticles
Sodium dodecyl sulphate and sitrate of sodium were used. Silver nitrate solution containing 1.0 mM and sodium dodecyl sulphate of concentration of 8 % w/w was used as a metal salt precursor and a stabilizing agent, respectively. Hy-drazine hydrate solution with a concentrate ranging of 1.0 mM and citrate of sodium solution of 1.0 mM was used as a reducing and stabilizing agents. The silver nanoparticles were purified by centrifugation and to remove excess silver ions, the silver colloids were washed at least three times with de-ionized water under nitrogen stream. The obtained dried powder of the nano-size silver was obtained. This solution was diluted by the solvent and samples of solutions
with different nanoparticles concentrations were obtained. Silver nanoparticles with different concentrations (0.05, 0.06, 0.07, 0.08, 0.09 mM) were used. Then, the right quantities were measured and used to coated thin glass substrates and kept for drying for 48 hours at room temperature [25].
Preparation of silver doped CH3NH3Pbl3 Thin films
Thin films of CH3NH3PM3 were prepared by solvent-solvent method as proposed [34]. The precursors was dissolved in a solvent called NMP, then Ag-NPs solution were added before coating was done onto a glass substrate. The coated substrate was bathed in diethyl ether DEE, a second solvent that selectively grabbed the NMP solvent and whisked it away leaving an ultra-smooth film of crystals.
Characterization of silver doped CHsNHjPbh Thin Films
Transmittance and reflectance was measured by a spectrophotometer within the wavelength range 300-900 nm. Optical parameters were determined through simulation using a computer program (Scout 2.4 software). Analysis was carried out to evaluate the optical properties and the interactions of intrinsic and extrinsic properties of Ag-CHsNHsPbl3 as modified by silver nanoparticles. An uncoated glass slide was used as a reference sample for determining transmittance, reflectance, and absorption to determine other optical constants like band gap and energy losses.
RESULTS AND DISCUSSION Crystal Structure
The crystal structure of was accepted in this work as developed by models in literature [2, 5, 13]. This formed the base of explaining the observations made in this work. Absorbance A, transmittance T and reflectance R was obtained for silver nanoparticles-doped hybrid perovskite thick films at different nanoparticles concentrations recorded over the wavelength range 300-900 nm using the UV-Vis Spectropho-tometer. The raw data was plotted to obtain curves using Origin Pro software. The interactions based on simulated data was analyzed and explained.
A crystal structure is composed of a unit cell, a set of atoms arranged in a particular way; which is periodically repeated in three dimensions on a lattice. A crystal structure is a unique arrangement of atoms in a crystal. The obtained doped hybrid perovskite thick films were examined and found to be uniform. Its optical quality was also good. The crystal structure of the precursor methyl ammonium lead tri-iodide is given in Figure 1.
Figure 1 - Chemical structure of CH3NH3PbI3 (A - CH3NH3, B - Pb, X - I)
Absorbance A
Although silver nanoparticles at different concentrations were used as follows, it was assumed that the thickness of the films was uniform. In this work, an average large thickness of 89 nm was obtained. Since absorbance is measure of the capacity of a substance to absorb light of a specified wavelength. It is equal to the logarithm of the reciprocal of the transmittance and therefore, the plot in Figure 2 depicted the variation absorbance against wavelength.
Figure 1 - Absorption spectra of silver-doped hybrid perovskite thick films at different concentrations
As depicted in Figure 2, the films exhibited strong broad band with peak absorption at around 530 nm wavelength. This absorption peak was similar to silver nanoparticles peak shown by silver nanoparticles of about 60 nm nano-size [9, 15, 16, 23]. It was also observed that absorbance varied within 10-17 % for all concentrations used.
concentrations used. It was observed that the value of reflectance R was minima for the low nanoparticles concentration of 0.05 mM at about 6.4 % at visible wavelength region. However, this reflectance increased with increasing silver nanoparticles concentrations till it attained a value of about 9.2 % at 0.09 mM at wavelength A of approximately 545 nm.
Transmittance T
Transmittance is the ratio of the radiant energy transmitted through a sample to the radiant energy incident on the surface of the sample. It is the fraction of incident electromagnetic power that is transmitted through a sample, in contrast to the transmission coefficient, which is the ratio of the transmitted to incident electric field. Transmittance reached as high as about 79 % for thick films containing low silver nanoparticles concentration of 0.05 mM. However, this decreased as silver nanoparticles concentration increased as depicted by Figure 3.
14
2
0 -1-1-.-T-1-
300 400 500 600 700 800 900
X (nm)
Figure 4 - Reflectance R spectra of the silver-doped hybrid films at different concentrations
Figure 3 - Absorption spectra of silver-doped hybrid perovskite thick films at different concentrations
Absorption Coefficient a
Absorption in the physics of materials can be defined based on a fractional amount that is proportional to the thickness of the layer. The change in energy as the wave passes through a layer is a constant of the material for a given wavelength and is called its absorption coefficient. The values of the absorption coefficients a was calculated using Equation 3 under the theoretical frame work. The variation plot of a, with the photon energy hv at different concentrations is depicted in Figure 5 with the photon energy range of 1.5-5.0 eV.
Reflectance R
Reflectance of a material defines how effective the surface reflects radiant energy. It is the fraction of incident electromagnetic power that is reflected at an interface. The reflectance spectrum or spectral reflectance curve is the plot of the reflectance as a function of wavelength. The spectrum curves of the reflectance of the thick films had a similar but inverted behavior to those of the absorbance as depicted in Figure 4.
This was therefore attributed to the correlation between reflectance and the absorbance for all
Figure 5 - The absorption coefficient for different silver nanoparticles concentrations
It was noted that the extinction coefficient a increased with increase the photon energy hv. A notable band gap occurred between photon energy 2.4-2.6 eV. This was attributed to the presence of silver nanoparticles having influenced the outcome of the absorbance or reflectance of the films [25, 27, 32]. The absorption coefficient varied varies within the range 2.1-4.2 cm-1 depending on silver nanoparticles concentrations.
Extinction Coefficient k
Extinction coefficient is also referred to as molar absorptivity in chemical engineering. It's a parameter that defines how strongly a substance absorbs light at a given wavelength, per mass density or per molar concentration, respectively. Using the calculated and simulated values of the corresponding a and Equation 5, extinction coefficient k was calculated for against incident photon energy hv and the results plotted in Figure 6 for different nanoparticles concentrations.
ized by the letter n or n in descriptive text and mathematical equations. The variation of the refractive index n with incident photon energy hv for different nanoparticles concentration s plotted in Figure 7 and it can be shown that the refractive index was within the range of 1.6-1.8 for the concentration used.
2.2 ■
16 • —0.05 DIM
14 ' -------------0.08 mM
-0.09 mM
1.2 -.-.---
1 2 3 4 5
hv (eV)
Figure 7 - The refractive index n versus the incident photon energy hv for different nanoparticles concentrations
Figure 6 - The extinction coefficient for different nanoparticles concentrations
The maximum obtained refractive index was the photon energy hv of about 2.2 eV.
Optical Conductivity <jopt and <elect
,opt and electrical <7eiect conductiv-
Both optical ao
ity were determined by using Equation 8 and Equation 9 respectively and the results obtained were plotted in Figure 8 for optical conductivity and Figure 9 for electrical conductivity respectively for different nanoparticles concentrations.
From the Figure 6, it can be noted that the variation of extinction coefficient was approximately similar to that of absorption coefficient. This was in agreement as this was equally portrayed by the direct relation between the two constants by Equation 5. Therefore, based on the findings, the extinction coefficient varies within the range 1.01.7 x 10- 5.
Refractive Index n
Refractive Index or index of Refraction is a value calculated from the ratio of the speed of light in a vacuum to that in a second medium of greater density [18]. Refractive index variable is symbol-
Figure 8 - The variation of the optical conductivity with the incident photon energy at different
concentrations
<
opt
Figure 9 - The variation of the electrical conductivity <'elect with the incident photon energy at different concentrations
Optical conductivity is a measure of electrical conductivity in an alternating field. This allows the dielectric constant as parameter comes into play when analyzing thin films which rules allowed propagations of light into matter. Evaluated optical conductivity refilled that it varied within the range 0.3-0.6 x 1010 sec-1.
Electrical conductivity is the measure of a material's ability to allow transport of an electric charge and it is taken as the ratio of the current density to the electric field strength. It is equivalent to the electrical conductance measured between opposite faces of a 1-metre cube of the material under test [14, 26]. Similarly, the electrical conductivity <Teiect was determined and it
was found out that it varied within the range 1.41.6 x 105 S cm-1. It was concluded that the value of < was noted to be high at the low photon energies and consequently decreased as the incident photon energy hv increased.
Optical band gap Eg
In hybrid perovskite semiconductors, electrons are confined to a number of allowed bands of energy, and forbidden bands of energy in other regions. Therefore, the term "band gap" refers to the energy difference between the top of the valence band and the bottom of the conduction band. Electrons are able to jump from one band to another. In this work, the values of the band gap E was determined form the simulated data
through the scout software, without using extrapolated technique where the linear part of the
1/2
plot Ohv versus the incident photon energy hv with abscissa [33, 34] is used. The simulated
band gap was tabulated in table 1 where it was observed that silver nanoparticles increased the band gab [15]. This was explained that increase in absorption coefficient a was not as a result of introducing silver dopant atoms but rather, it was due to the change and realignment of the crystal structure. This was attributed to the crystal defects. It was assumed that the rotation of the PI3 octet may have been restricted to rotate and as a result, the interaction of the Valence band and conduction band may have shifted resulting to increased band gap [6, 14, 17]. From Table 1, it was concluded that the band gap of the CH3NH3Pbl3 hybrid perovskite film was modified significantly by the presence of silver nanoparti-cles resulting into a decreased band gap from 1.921-1.832 eV [9, 27, 32].
Table 1 - Band gap E at different concentrations
Sample Silver nanoparticles concentration, mM Energy band gap Eg, eV
A 0.05 1.921
B 0.06 1.902
C 0.07 1.883
D 0.08 1.867
E 0.09 1.832
This was attributed to a creation or inhalation of both structural and point defects within the optical energy band gap.
CONCLUSIONS
In this work, silver nanoparticles were used to dope CHsNHsPbh hybrid perovskite thin films using the solution technique at room temperature. Optical properties were investigated and determined for different silver nanoparticles concentrations where the results showed that the thin films had highest transmittance of about 79 % while its band gap varied from 1.9211.832 eV. Electrical conductivity was 1.4-1.6 x 105 S cm-1 while optical conductivity varied within the range 0.3-0.6 x 1010 sec-1. The refractive index was within the range of 1.6-1.8 which was significantly low for optical applications. Finally extinction coefficient varied in the range 1.0-1.7 x 10- 5 while absorption coefficient varied within the range 2.1-4.2 cm-1. It was concluded that the thin films grown were suitable for photonic device applications.
ACKNOWLEDGEMENTS
The authors appreciate the laboratory technicians of the Department of Pure and Applied Science of Technical University of Mombasa for aid-
ing and performing photo spectrometric measurements.
REFERENCES
1. Abate, A., Saliba, M., Hollman, D. J., Stranks, S. D., Wojciechowski, K., Avolio, R., ... Snaith, H. J. (2014).
Supramolecular Halogen Bond Passivation of Organic-Inorganic Halide Perovskite Solar Cells. Nano Letters, 14(6), 3247-3254. doi: 10.1021/nl500627x
2. Agarwal, S., & Nair, P. R. (2014). Performance optimization for Perovskite based solar cells. In 2014
IEEE 40th Photovoltaic Specialist Conference (PVSC). doi: 10.1109/pvsc.2014.6925202
3. Agarwal, S., & Nair, P. R. (2015). Device engineering of perovskite solar cells to achieve near ideal ef-
ficiency. Applied Physics Letters, 107(12), 123901. doi: 10.1063/1.4931130
4. Ball, J. M., Lee, M. M., Hey, A., & Snaith, H. J. (2013). Low-temperature processed meso-
superstructured to thin-film perovskite solar cells. Energy & Environmental Science, 6(6), 17391743. doi: 10.1039/c3ee40810h
5. Burschka, J., Pellet, N., Moon, S.-J., Humphry-Baker, R., Gao, P., Nazeeruddin, M. K., & Grätzel, M.
(2013). Sequential deposition as a route to high-performance perovskite-sensitized solar cells. Nature, 499(7458), 316-319. doi: 10.1038/nature12340
6. Collavini, S., Völker, S. F., & Delgado, J. L. (2015). Understanding the Outstanding Power Conversion
Efficiency of Perovskite-Based Solar Cells. Angewandte Chemie International Edition, 54(34), 9757-9759. doi: 10.1002/anie.201505321
7. Eames, C., Frost, J. M., Barnes, P. R. F., O'Regan, B. C., Walsh, A., & Islam, M. S. (2015). Ionic transport in
hybrid lead iodide perovskite solar cells. Nature Communications, 6, 7497. doi: 10.1038/ncomms8497
8. Eperon, G. E., Burlakov, V. M., Docampo, P., Goriely, A., & Snaith, H. J. (2013). Morphological Control
for High Performance, Solution-Processed Planar Heterojunction Perovskite Solar Cells. Advanced Functional Materials, 24(1), 151-157. doi: 10.1002/adfm.201302090
9. Gardini, D., Christensen, J. M., Damsgaard, C. D., Jensen, A. D., & Wagner, J. B. (2016). Visualizing the
mobility of silver during catalytic soot oxidation. Applied Catalysis B: Environmental, 183, 28-36. doi: 10.1016/j.apcatb.2015.10.029
10. Gonzalez-Pedro, V., Juarez-Perez, E. J., Arsyad, W.-S., Barea, E. M., Fabregat-Santiago, F., Mora-Sero,
I., & Bisquert, J. (2014). General Working Principles of CHsNHsPbXs Perovskite Solar Cells. Nano Letters, 14(2), 888-893. doi: 10.1021/nl404252e
11. Jeon, N. J., Noh, J. H., Kim, Y. C., Yang, W. S., Ryu, S., & Seok, S. I. (2014). Solvent engineering for high-
performance inorganic-organic hybrid perovskite solar cells. Nature Materials, 13(9), 897-903. doi: 10.1038/nmat4014
12. Im, J.-H., Lee, C.-R., Lee, J.-W., Park, S.-W., & Park, N.-G. (2011). 6.5% efficient perovskite quantum-
dot-sensitized solar cell. Nanoscale, 3(10), 4088-4093. doi: 10.1039/c1nr10867k
13. Kojima, A., Teshima, K., Shirai, Y., & Miyasaka, T. (2009). Organometal Halide Perovskites as Visible-
Light Sensitizers for Photovoltaic Cells. Journal of the American Chemical Society, 131 (17), 60506051. doi: 10.1021/ja809598r
14. Lang, L., Yang, J.-H., Liu, H.-R., Xiang H. J., & Gong, X. G. (2014). First-principles study on the elec-
tronic and optical properties of cubic ABX3 halide perovskites. Physics Letters A, 378(3), 290293. doi: 10.1016/j.physleta.2013.11.018
15. Li, Z., Zhang, M., Cheng, D., & Yang, R. (2016). Preparation of silver nano-particles immobilized onto
chitin nano-crystals and their application to cellulose paper for imparting antimicrobial activity. Carbohydrate Polymers, 151, 834-840. doi: 10.1016/j.carbpol.2016.06.012
16. Lou, X., Pan, H., Zhu, S., Zhu, C., Liao, Y., Li, Y., ... Chen, Z. (2015). Synthesis of silver nanoprisms on
reduced graphene oxide for high-performance catalyst. Catalysis Communications, 69, 43-47. doi: 10.1016/j.catcom.2015.05.021
17. Minemoto, T., & Murata, M. (2014). Device modeling of perovskite solar cells based on structural
similarity with thin film inorganic semiconductor solar cells. Journal of Applied Physics, 116(5), 054505. doi: 10.1063/1.4891982
18. Mosconi, E., Amat, A., Nazeeruddin, M. K., Grätzel, M., & De Angelis, F. (2013). First-Principles Mod-
eling of Mixed Halide Organometal Perovskites for Photovoltaic Applications. The Journal of Physical Chemistry C, 117(27), 13902-13913. doi: 10.1021/jp4048659
19. Nie, W., Tsai, H., Asadpour, R., Blancon, J.-C., Neukirch, A. J., Gupta, G., ... Mohite, A. D. (2015). High-
efficiency solution-processed perovskite solar cells with millimeter-scale grains. Science, 347(6221), 522-525. doi: 10.1126/science.aaa0472
20. Noel, N. K., Stranks, S. D., Abate, A., Wehrenfennig C., Guarnera, S., Haghighirad, A.-A., ... Snaith, H. J.
(2014). Lead-free organic-inorganic tin halide perovskites for photovoltaic applications. Energy & Environmental Science, 7(9), 3061-3068. doi: 10.1039/c4ee01076k
21. Noh, J. H., Im, S. H., Heo, J. H., Mandal, T. N., & Seok, S. I. (2013). Chemical Management for Colorful,
Efficient, and Stable Inorganic-Organic Hybrid Nanostructured Solar Cells. Nano Letters, 13(4), 1764-1769. doi: 10.1021/nl400349b
22. Saoud, K., Alsoubaihi, R., Bensalah, N., Bora, T., Bertino, M., & Dutta, J. (2015). Synthesis of sup-
ported silver nano-spheres on zinc oxide nanorods for visible light photocatalytic applications. Materials Research Bulletin, 63, 134-140. doi: 10.1016/j.materresbull.2014.12.001
23. Sha, W. E. I., Ren, X., Chen, L., & Choy, W. C. H. (2015). The efficiency limit of CHsNHsPbIs perovskite
solar cells. Applied Physics Letters, 106(22), 221104. doi: 10.1063/1.4922150
24. Shabani Shayeh, J., Ehsani, A., Ganjali, M. R., Norouzi, P., & Jaleh, B. (2015). Conductive poly-
mer/reduced graphene oxide/Au nano particles as efficient composite materials in electrochemical supercapacitors. Applied Surface Science, 353, 594-599. doi: 10.1016/j.apsusc.2015.06.066
25. Snaith, H. J. (2013). Perovskites: The Emergence of a New Era for Low-Cost, High-Efficiency Solar
Cells. The Journal of Physical Chemistry Letters, 4(21), 3623-3630. doi: 10.1021/jz4020162
26. Sönnichsen, C., Franzi, T., Wilk, T., Plessen, G. von, & Feldmann, J. (2002). Plasmon resonances in
large noble-metal clusters. New Journal of Physics, 4, 93-93. doi: 10.1088/1367-2630/4/1/393
27. Stranks, S. D., Eperon, G. E., Grancini, G., Menelaou, C., Alcocer, M. J. P., Leijtens, T., ... Snaith, H. J.
(2013). Electron-Hole Diffusion Lengths Exceeding 1 Micrometer in an Organometal Trihalide Perovskite Absorber. Science, 342(6156), 341-344. doi: 10.1126/science.1243982
28. Sun, X., Asadpour, R., Nie, W., Mohite, A. D., & Alam, M. A. (2015). A Physics-Based Analytical Model
for Perovskite Solar Cells. IEEE Journal of Photovoltaics, 5(5), 1389-1394. doi: 10.1109/jphotov.2015.2451000
29. Umari, P., Mosconi, E., & De Angelis, F. (2014). Relativistic GW calculations on CH3NH3PbI3 and
CH3NH3SnI3 Perovskites for Solar Cell Applications. Scientific Reports, 4(1). doi: 10.1038/srep04467
30. Wang, U. (2014, September 28). Perovskite Offers Shot at Cheaper Solar Energy. Retrieved from
https://www.wsj.com/articles/perovskite-offers-shot-at-cheaper-solar-energy-1411937799
31. Wei, L., Lu, J., Xu, H., Patel, A., Chen, Z.-S., & Chen, G. (2015). Silver nanoparticles: synthesis, proper-
ties, and therapeutic applications. Drug Discovery Today, 20(5), 595-601. doi: 10.1016/j.drudis.2014.11.014
32. Xiao, Z., Bi, C., Shao, Y., Dong, Q., Wang, Q., Yuan, Y., ... Huang, J. (2014). Efficient, high yield
perovskite photovoltaic devices grown by interdiffusion of solution-processed precursor stacking layers. Energy & Environmental Science, 7(8), 2619-2623. doi: 10.1039/c4ee01138d
33. You, J., Hong, Z., Yang, Y. (Michael), Chen, Q., Cai, M., Song, T.-B., ... Yang, Y. (2014). Low-
Temperature Solution-Processed Perovskite Solar Cells with High Efficiency and Flexibility. ACS Nano, 8(2), 1674-1680. doi: 10.1021/nn406020d
34. Zhou, Y., Yang, M., Wu, W., Vasiliev, A. L., Zhu, K., & Padture, N. P. (2015). Room-temperature crystal-
lization of hybrid-perovskite thin films via solvent-solvent extraction for high-performance solar cells. Journal of Material Chemistry A, 3(15), 8178-8184. doi: 10.1039/c5ta00477b